Galvanizing refers to the surface treatment technology of plating a layer of zinc on the surface of metal, alloy or other materials to play the role of aesthetics and rust prevention. The main method used now is hot galvanizing. However, hot dip galvanizing industry has been developed with the rapid development of cold strip rolling in the past 30 years. The production process of hot-galvanized sheet mainly includes: raw plate preparation → pre-plating treatment → hot-dip plating → post-plating treatment → finished product inspection and so on.

4. Substrate material: The substrate material of electrogalvanized wire also has a certain impact on its corrosion resistance. The substrate of different materials has different chemical properties and electrochemical activities, and the corrosion performance is different under different environmental conditions, and the compatibility with zinc layer will also have a certain impact on the corrosion performance.

In order to pack and bundle galvanized wire on the surface of the deposit layer to remove the surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is caused by soaps and saponable fatty surfactants being brought into the tank. Moderate foam formation rates may be harmless. Small homogeneous particles of large denier present in the tank can stabilize the foam layer. To remove surface active substances by matting with activated carbon. Or filtration to make the foam less stable, which are effective measures; Other measures should also be taken to reduce the intake of surfactant. The electroplating speed can be significantly reduced by the introduction of organic matter. Although the chemical formula is conducive to a high deposition rate, the coating thickness cannot meet the requirements after the organic matter is loaded, so activated carbon can be used to treat the tank.

6, according to the wire diameter thickness to adjust zinc dipping time. Zinc dipping time should be adjusted according to the thickness of wire diameter. The method of adjustment is the length of the distance between the lead screw on the zinc pot and the ceramic sinking roll. The zinc dipping time of coarse wire diameter should be long, and the zinc dipping time of fine wire diameter should be short.