chain mesh fencing

No less than 5 disks should be extracted from each inspection lot for diameter error inspection. 1 point of steel wire should be extracted from each disk to measure steel wire diameter, and the actual diameter of steel wire at this point should be taken as the average value of the two vertical directions. The diameter error of cold-drawn low carbon steel wire should conform to the rules in the table below. The unqualified inspection batches shall be checked one by one, and the qualified batches can be used for engineering.

The tensile strength of cold drawn spring steel wire is slightly higher than that of oil tempered steel wire. The large specification of cold drawn steel wire elastic force is too large, winding the spring is very difficult, so the cold drawn spring steel wire application specification is generally less than 8.0mm, oil quenching tempered steel wire application specification is generally less than 13.0mm. In fact, the diameter of 13.0mm spring is used to light tension spring steel wire, cold drawing wound made into shape and then quenched and tempered. Steel wire with diameter above 15.0mm is mostly made by heating winding process.

Because of the high carbon content, simple cracks occur during water quenching, so double liquid quenching (water quenching + oil cooling) is mostly used, and oil quenching is mostly used for small cross section parts. This type of steel is generally used after quenching by medium temperature tempering or normalizing or in the surface quenching state. Mainly used for manufacturing spring and wear-resistant parts.

Hot dip galvanizing, also known as hot dip galvanizing, is a method of obtaining a metal covering by immersing a steel member in a molten zinc solution. With the rapid development of high-voltage transmission, transportation and communication, the protection requirements for steel parts are becoming higher and higher, and the demand for hot-dip galvanizing is also increasing. Usually the thickness of electric galvanized layer is 5 ~ 15μm, and the large roll galvanized wire layer is generally more than 35μm, even up to 200μm. Hot dip galvanizing has good covering ability, dense coating and no organic inclusions.