making a wire trellis

Galvanized iron wire is very common in practical application, some people think that galvanized iron wire will not rust, in fact, it is not. Metal corrosion is caused by the chemical or electrochemical action of the surrounding medium. According to different media, it is divided into atmospheric corrosion, soil corrosion, seawater corrosion, bacterial corrosion and so on. Atmospheric corrosion is more common, because metal products in the process of processing, transportation and storage, when in contact with the atmosphere, there are always atmospheric corrosion conditions.

The electrode is a kind of material that the coating (that is, the coating) is uniformly and centrally applied on the welding core outside the metal welding core. The electrode is composed of two parts: the welding core and the coating. The welding core is the metal core of the electrode. In order to ensure the quality and performance of the weld, there are strict regulations on the content of various metal elements in the welding core.

Dip plastic six side barbed wire corrosion lost the original characteristics, in the shape, color and mechanical properties and other aspects will change, resulting in equipment damage, pipeline leakage, in particular, is prone to fracture, lose the original protective function.

Different supports are used for different installation environments. In the past, the blade barbed wire was not easy to fix, and the installation environment was often steep. Therefore, special tools must be used to fix the blade barbed wire to prevent it from being improperly installed.

Some customers are just for ordinary fencing, but the pictures provided to the barbed rope factory are indeed applied to the barbed rope products in prison, maybe because the customers prefer the style, but such products are really a little overqualified to be installed in ordinary areas. Even if the customers prefer such barbed rope products, the higher price is prohibitive. The price and quality of the prison rope are certainly not the level of the rope we contact in our daily life.

On the highway, the barbed wire protective net is generally used to prevent people and animals from crossing the highway at will, so as not to interfere with driving and reduce accidents, as well as effectively prevent illegal occupation of highway land and other issues of traffic safety facilities. There are many forms of barbed wire protective nets, commonly used are metal, woven nets, barbed wire and evergreen green gracilaria. In the densely populated areas set up metal woven net, people and animals are less sparse areas of the form of barbed wire, in the toll station, service area and other sections of the structure of hedge and barbed wire. In the past two years, considering the aesthetic problem, some highways in the Pearl River Delta region adopted the fruit plastic spot welding mesh (usually said guardrail mesh), the barbed wire protective mesh is more beautiful, but also durable, the overall effect is good, but the construction requirements are higher, more expensive. General sections should not be used, in the city center, scenic spots or strong requirements for beauty of the section available.

Raw material of wire mesh sheet cold drawn low carbon steel wire base material can choose low carbon steel hot rolled disk bar or hot rolled smooth steel bar. The base material number and diameter of cold-drawn low carbon steel wire can be confirmed according to the rules in the table below. During the cold drawing process, the surface shrinkage rate of each drawing should not be greater than the wire mesh before cold drawing. Annealing shall not be carried out during wire drawing. If butt welding is required, the same production unit and base material of the same number should be selected. The appearance quality of wire mesh should not affect wire drawing. When the welding function is poor or brittle fracture occurs, special inspection should be carried out according to relevant standards.

Hot dip galvanizing, also known as hot dip zinc and hot dip galvanizing, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to play the purpose of anticorrosion.

When the large roll galvanized wire galvanizing process coating foaming, first check the bath temperature. If the bath temperature is not low, then strengthen the plating before removing oil, prevent the matrix metal in acid corrosion. If you pay attention to these problems, the foaming phenomenon still exists, it should pay attention to the amount and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, in order to reduce the content of additives, observe whether the foaming phenomenon is improved. If there is still no improvement, it is necessary to check whether the storage period of additives is too long, or whether there are too many impurities in the additives.