aluminium mosquito net for windows price

For key and important parts with tensile strength greater than 1034Mpa, the stress should be removed at 200±10℃ for more than 1 hour before plating, and for carburized or surface hardened parts, the stress should be removed at 140±10℃ for more than 5 hours. The cleaning agent used for cleaning shall have no effect on the binding force of the coating and no corrosion on the substrate. Acid activation Acid activation solution should be able to remove corrosion products and oxide film (skin) on the surface of parts without excessive corrosion on the matrix.

Therefore, when the zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms are diffused with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with the iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with the zinc and sinks into the bottom of the hot galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.

Select cut wire first of all to ensure that the raw material of the silk is exactly the raw material you need, the raw material to ensure that it will be used well. Choose the straightness is relatively high, so that the length of the truncation will be the same, there will not be a lot of length difference, the length of the truncated wire is a very important element to select the truncated wire.

The protective duration of galvanized iron wire is closely related to the thickness of galvanized iron wire. In general, zinc layer thickness needs to be very high in dry main gas and indoor applications, but in harsh environments. Therefore, in the selection of galvanized layer thickness, the impact of the environment should be considered. If galvanized iron wire products of different diameters are required, material selection and coating should be controlled reasonably.