electrowelded mesh

In the electroplating tank through the current unidirectional make zinc plating on the metal surface gradually, the production speed is slow, the coating is uniform, the thickness is thin, usually only 3-15 micron, the appearance is bright, smooth, beautiful, poor corrosion resistance, generally will rust in a few months. The production process of hot wire plating mainly includes: preparation of the original plate → pre-plating treatment → hot dip plating → post-plating treatment → finished product inspection, etc. According to custom often according to plating pretreatment method.

If the zinc coating is good, but when the light comes out in 3% nitric acid, there is a dark shadow on the coating, and the film is brown when passivation occurs, which may be caused by foreign metal impurities such as copper or lead in the galvanized liquid. When there is a problem in the process of galvanizing, check the temperature and current density first, and then measure and adjust the content of zinc and sodium hydroxide in the bath through the analysis of the bath. Whether DPE levels are low can be determined by Hull cell test.