“Dry” hot dip galvanizing is also called “drying solvent method” hot dip galvanizing. Iron and steel work pieces through degreasing, pickling, cleaning, dipping aid solvent and drying, and then immersed in the molten zinc solution to galvanize. The co-solvent is usually hydrochloric acid, ammonium chloride, or ammonium chloride mixed with zinc chloride in aqueous solution.

Hot dip galvanizing is to remove oil from the workpiece, pickling, dipping, drying after dipping into the dissolved zinc solution for a certain time, can be brought out. Hot dip galvanizing is an effective way to prevent corrosion of metal. It is mainly used for metal structure facilities in various industries. It is to immerse the steel parts after rust removal into the melting zinc liquid at about 500℃, so that the surface of the steel members is attached with zinc layer, so as to play the purpose of anti-corrosion. The galvanized layer is more firm.

The technical term “galvanized” means that metal has been specially treated with zinc. Essentially, the wire is covered with a very thin layer of zinc. It is this thin layer of zinc that gives galvanized wire its many properties. Galvanizing can be done by dipping wire into a pool of zinc or by electroplating.

There is no adhesion test of powder spraying or fluorocarbon spraying on packaged galvanized wire, but there are two points for reference: first, in sealed or air-free environment, non-metallic volatiles can corrode zinc coating; Second, zinc at higher than 230 degrees (c) will cause the matrix metal brittle. And powder spraying and fluorocarbon spraying are to be baked at a higher temperature and in a sealed environment, causing rapid corrosion of zinc, resulting in loose corrosion film resulting in coating adhesion decline, and even lead to (matrix) steel wire brittle situation may exist.