Therefore, when the zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms are diffused with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with the iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with the zinc and sinks into the bottom of the hot galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.

During this process, each time the wire is pulled over, the surface hardens due to the high friction temperature. So basically every time you pull it you have to annealing it in the furnace. On the one hand, it is to reduce the surface hardness. On the other hand, during the process of wire pulling, only the surface is deformed, and the center is unchanged. So there’s a lot of stress inside. Therefore, it is necessary to rely on annealing to eliminate the internal stress, so that the wire becomes soft again to eliminate the stress before being drawn again.

(3) Can realize butt joint, Angle joint, lap joint, T joint and other joint forms of welding.

Copper sulfate point test is a simple way to quickly distinguish ordinary carbon steel and all types of stainless steel wire rope. The concentration of copper sulfate solution used is 5%-10%. Before the point test, the experimental area should be thoroughly removed from the oil or other impurities, and a small area should be polished by grinding machine or soft grinding cloth, and then the test liquid drops to the grinding place. Ordinary carbon steel or iron in a few seconds will form a layer of outer metal copper, and the surface of stainless steel does not produce copper precipitation or display copper color.