3, reduce the bivalent iron ion in the plating aid used for hot plating wire, reduce the formation of zinc slag

Secondly, the zinc-iron alloy protective layer of hot-dip galvanized wire has self-healing properties. When the surface of hot-dip galvanized wire is damaged or scratched, zinc metal can form zinc ions through electrochemical reaction, self-healing repair of the damaged zinc-iron alloy protective layer, so as to maintain the corrosion resistance of the steel wire. This self-healing property enables the hot-dip galvanized wire to be quickly repaired during use, even if there is a slight scratch or damage on the surface, avoiding further corrosion. After the ordinary steel wire is damaged on the surface, it is often unable to repair itself, which is easy to lead to the diffusion of corrosion and accelerate the aging and damage of the steel wire.