Of course, the quality of any kind of product is also affected by the implementation of the specification of the manufacturer, if it is the welding screen manufacturers in the production of their own is not very high implementation of the specification, or in the production line of the procedure specification has declined, or there is no higher requirements on the production link.

The reason why there are black spots in wire mesh welding is that the action of wire feeding should be timely filled in the melting time, and the development should be appropriate. There is no argon gas, long burning, large current, long distance, blunt tungsten needle and high molten pool temperature are the fundamental reasons for blackening. Continuous burning, is about active welding machine energy selection, machine welding will appear black spots.

Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.