construction wire mesh

Wire rod to stop normalizing or soxaustenitizing treatment, large specifications with spheroidizing annealing instead. In the middle, especially before the waste product drawing process of thermal disposal throughout the selection of soxaustenitizing disposal. Decarbonization should be prevented during thermal disposal. Sulfuric acid or hydrochloric acid pickling was used to remove the oxide sheet after hot treatment. Coating (see lubrication carrier) can be dipped in lime, phosphating, borax disposal or copper plating.

Reverse twist barbed rope: first wrap the barbed wire around the main wire (i.e. a single wire) and then add another wire to twist and weave it into a double strand barbed rope.

One is to do a good job of galvanized wire packaging, avoid bump, to ensure the integrity of the zinc layer;

The thorn rope belongs to the weaving industry, so it is less affected by environmental protection. The thorn rope will not be discarded in the production process, and it belongs to the weaving industry, so the situation is less affected by environmental protection.

Now large roll galvanized wire in our life the use of more and more, to galvanized wire products bring a great market, galvanized wire products are more and more types. The surface coating of good quality galvanized wire is continuous and smooth. When the plating parts are installed and combined, there can be no flow hanging, slag or drop remaining, and no surface defects such as iron exposure. Good quality galvanized wire, coating must be uniform, roughly uniform in copper sulfate solution soaking five times without exposing iron. And with hammering test does not bulge, do not fall off. This is a good galvanized wire should have characteristics.

Stainless steel barbed rope in the way of corrosion is not very, because the surface is not treated but rely on its own raw materials for corrosion resistance, so there will be no chemical reaction. After a long time of use, it will not rust like the corrosion layer on the surface of hot dip galvanized barbed rope, because the internal material of stainless steel barbed rope is the same as the material on the surface. The most obvious difference in a short time is the cross section of this piece, hot dip galvanized barbed wire because of surface anticorrosion treatment, so there will be rust in the cross section of this piece, and stainless steel barbed wire because the internal raw materials and surface raw materials are consistent, so there is no such situation.

The barbed rope produced by the barbed rope factory adopts the way of winding in order to facilitate transportation, and the disk weight of the galvanized barbed rope is different according to the size.

The barbed rope factory not only provides the sales work of blade barbed rope, including the subsequent construction, but also contracted together, and the construction price is particularly different.

When galvanized wire out of the light plating should be carried out light treatment. The bath temperature of galvanized wire should be controlled well. Galvanized wire, also known as hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to play the purpose of anticorrosion.

Galvanized wire A stable layer of zinc is coated on the outside of the wire, which is used to protect the wire and make the wire service life longer. When producing galvanized wire, the wire is pickled. Pickling is to use some acid mist or acid to wash off some oxides on the surface of iron, that is, rust, and some other corrosive substances, to achieve the purpose of cleaning iron, so that zinc will fall off when galvanizing.