4 common nail

Dip is one of the anticorrosion methods of galvanized diamond net. For hook mesh immersion is one of the methods of anti-corrosion, now the domestic more mature method is: powder immersion method, it originated from the fluidized bed method, the so-called fluidized bed is used in the Winkler gas furnace on the oil contact decomposition, and then developed the solid-gas two-phase contact process, gradually used in metal coating. So sometimes it is still called “fluidized bed coating method”, the actual process is to add the powder coating to the bottom of the porous, breathable container, the blower from the bottom into the treated compressed air, so that the powder coating turned to the “fluidization state”. It becomes a fine, evenly distributed powder.

The breeding galvanized electric welding net is still in the construction project and has been well used. It is because of such a network, so now in the construction project, can save more time and effort. Not only in this industry, such as breeding and breeding in nursery stock and supermarket shelves, have started to use such nets, to meet the needs of the industry, and can also well help people in their jobs.

Low and medium carbon steel wire is used as raw material, with good surface gloss, uniform zinc layer, strong adhesion, corrosion resistance and so on. Available: diameter 1.60mm-4mm (16#-33#) cold plating wire; Diameter 6.40mm-0.81mm(8#-21#) black iron wire, changed wire. It is mainly used in communication equipment, medical equipment, weaving net, brush, steel cable, filter, high-pressure pipe, construction, crafts and other industries.

Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.