1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.

Electric welding net welding after galvanized is after the completion of the welding and then cold galvanized or hot galvanized; After the first galvanized welding is to change the wire welding mesh, welding can be seen after the completion of the welding spot; The two processes are different prices are also very different, the cost of the first plating after welding is low, the surface is smooth, and the cost of the first welding after plating is higher, not easy to rust.

Cold galvanizing is in the plating tank through the current unidirectional zinc gradually plated on the metal appearance, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, smooth, high aesthetics, poor corrosion resistance, generally a few months will rust. Hot dip galvanized coating is thicker, generally 30-60 microns, coating corrosion resistance is higher. Suitable for outdoor work of steel parts, such as highway fences, power towers, large size fasteners and other more “rough” workpiece long-term rust prevention.