The production process of large coil galvanized wire is relatively simple. The wire after cleaning is put into electroplating solution first. Of course, the plating solution should contain zinc oxide, a direct current of steel, another zinc plate in the plating solution. The zinc is transferred to the surface of the steel as a molecule. If it shows a bright and beautiful color, the wire is coated with zinc.

There are many categories of large coils of galvanized wire, and different categories can be applied to different scenarios. Galvanized iron wire common application is the application of the construction industry, one is the use of binding wire, whether it is the binding of scaffolding or reinforcement, need galvanized iron wire to carry out, the common specifications are 22 and 24 wire, common length of 30cm, 35cm, 40cm, 45cm, 50cm. There is also 20kg or 50kg a bundle of 18, 16, 14, 12, 10 galvanized coil wire.

In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.

The temperature of large roll galvanized wire should be controlled at 30 to 50℃ during electroplating. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used. Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device.