perforated metal material

Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, Softness is also very uniform, color is also consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding coat hanger, reprocessing industry and so on.

The composition of hot dip galvanizing layer is composed of hot dip galvanizing layer, which is composed of iron zinc alloy between iron matrix and surface pure zinc layer. The shape of the workpiece is formed by the iron zinc alloy layer in hot dip, so that the iron and pure zinc layer touch outstanding. When the iron workpiece is immersed in a molten zinc solution, the initial zinc and iron (body) are formed at the interface. This is a crystal made up of zinc atoms in the solid metal iron. When two metal atoms are fused together, the gravitational force between the atoms is very small.

Stainless steel barbed rope is in the material aspect of protection so durability is also better, these two products are known for long service life, but is high in price.

This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.