construction chain link fence

Razor blade barbed rope has been widely used in military sites, prisons, government agencies, banks in the world. The walls of living quarters, private homes, villas, fences, doors and Windows, highways, railway guardrail and border lines and other protection and security.

Some customers just use ordinary fences, but the pictures provided to the barbed rope factory are really used in the barbed rope products of prison, maybe because the customers prefer the style, but such products are really a little overqualified to be installed in ordinary areas. Even if customers prefer such barbed rope products, the high price is also prohibitive. The price and quality of the prison application barbed rope is certainly not the level of the barbed rope we contact in daily life.

Annealing wire is widely used because it has a good elasticity and flexibility, in the annealing process can be good control of its hardness, it is mainly made of iron wire, more often used in the construction industry binding wire use. In the production of the wire factory, annealing wire will be processed according to the properties of the material, according to the needs of different to change its hardness degree, can make it has more advantages, can reduce the consumption of metal, reduce the cost of production.

If the zinc coating is good, but when the light comes out in 3% nitric acid, there is a dark shadow on the coating, and the film is brown when passivation occurs, which may be caused by foreign metal impurities such as copper or lead in the galvanized liquid. When there is a problem in the process of galvanizing, check the temperature and current density first, and then measure and adjust the content of zinc and sodium hydroxide in the bath through the analysis of the bath. Whether DPE levels are low can be determined by Hull cell test.

Hot dip galvanizing is in the hot melt zinc liquid dip plating, production speed, thick but uneven coating, the market allows the low thickness of 45 microns, up to 300 microns above. It is dark in color, consumes more zinc metal, forms infiltration layer with base metal, and has good corrosion resistance. Hot dip galvanizing can be maintained for decades in outdoor environment.

Cold wire drawing is mainly used in the production of hardened low carbon steel wire, with a diameter of 8 mm steel bar to play a fixed role in the development of the construction industry has played a role in promoting the development of the construction industry, widely used. The bonding and anchorage performance between cold wire drawing and concrete is good. When used in components, the phenomenon of cracking in the anchorage area of components and damage caused by steel wire slip is fundamentally eliminated, and the bearing capacity and anti-cracking capacity of the end of components are improved.

On the contrary, the denser the ion deposition, the better the quality of zinc layer. Under the condition that the surface zinc layer is dense and bright, the quality of zinc layer per unit area should reach 80g/m2, and the process parameters should be optimized as follows: current density is 16-20A /dm2, mass concentration of zinc sulfate solution is 500g/L, and pH value is 2.5-3.0.

Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, The softness is also very uniform, the color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry, etc.