Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

In order to remove defects such as surface film layer and surface inclusion of large roll galvanized wire, it can be treated by conventional technology. The presence of small homogeneous particles of large denier in the tank can stabilize the foam layer, but the accumulation of too many solid particles can cause explosion. Activated carbon mat to remove surface active substances, or through filtration to make the foam less stable, these are effective measures; Other measures should also be taken to minimize the intake of surface active substances. The electroplating speed can be significantly reduced by the introduction of organic matter.

Galvanized also has several different methods, the so-called hot dip galvanizing is put racing in the zinc bath, need to clean them on metal, which ensures that formed between metal and coating adhesive, after cleaning, the matrix metal is dissolved, to clear any residual oxides of residue and then immerse the substrate metal heating liquid zinc, and metallurgical bonding is formed.

2. Eliminate caked zinc residue on zinc liquid surface

Preparation process: single twist plait, double twist plait.