perforated plate manufacturers

This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.

The production process of large coil galvanized wire is relatively simple. The wire after cleaning is put into electroplating solution first. Of course, the plating solution should contain zinc oxide, a direct current of steel, another zinc plate in the plating solution. The zinc is transferred to the surface of the steel as a molecule. If it shows a bright and beautiful color, the wire is coated with zinc.