B. When the thickness of the plating is greater than 4 mm, the zinc adhesion should not be less than 610g/m, that is, the average thickness of the zinc layer should not be less than 86 microns.

In the cattle net generally also PVC plastic PVC plastic is coated with a layer of dark green or gray brown plastic mold on the original galvanized steel wire, to avoid the corrosion of the wire diameter, is conducive to the improvement of the wire diameter corrosion prevention and rust prevention function. So the better the raw material, the higher the price. Zinc aluminum alloy cattle mesh is the best metal mesh on the market, the price is higher than hot dip galvanized raw materials. The service life is about 80-90 years, excellent anticorrosion function.

Hot dip galvanized coating is also relatively thick, but there is an uneven situation, for example, the thickness of the thin is only 45 microns, thick can reach 300 microns or even thicker, the color of this product is relatively dark. There is also a lot of zinc consumed in the production process. Zinc will form an infiltration layer with the metal. Its advantage is that it has good corrosion resistance. Electrogalvanizing, it is through the plating tank in the zinc one-way plating on the outside of the metal products, this way of making products is relatively slow, but its thickness is more uniform.

The impregnated hexagonal wire mesh will lose its original characteristics after corrosion, and will change in shape, color and mechanical properties, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break and lose the original protection function. Usually there are three kinds of metal corrosion: physical corrosion, chemical corrosion, electrochemical corrosion, corrosion in addition to the chemical properties and organizational structure of the metal itself, but also related to the surrounding medium, such as wet environment than dry environment easy corrosion, more impurities than impurities less easy corrosion, high temperature conditions than low temperature conditions easy corrosion. After understanding these, we can effectively prevent the corrosion of impregnated hexagonal wire mesh, prolong the service life of products.

Different hot dip galvanizing process is divided into two categories of annealing outside the line and annealing in the line, hot dip galvanizing is in the hot melt zinc liquid immersion plating, production speed, thick but uneven coating, the market allows Z low thickness of 45 microns, Z high can reach more than 300 microns. It is dark in color, consumes more zinc metal, forms infiltration layer with base metal, and has good corrosion resistance. Hot dip galvanizing can be maintained for decades in outdoor environment.