Stainless steel blade barbed rope production process is basically similar to galvanized blade barbed rope production process, usually according to the mold to determine the size of the blade.

After annealing, the extension rate of galvanized wire is increased, making the product more soft and increasing the scope of application of galvanized wire. After electric galvanized hot galvanized, electroplated copper and other widely used screen production. Building reinforcement binding with galvanized wire mesh braided with the first after plating, plating and other methods, after treatment of galvanized wire mesh or steel wire mesh, has good corrosion resistance, oxidation resistance characteristics, can be used in construction, petroleum, chemical, aquaculture, garden protection, food processing and other industries reinforcement, protection and heat preservation.

The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.