1.2 mm galvanised wire

The drawing process of the waste product has a great influence on the function of the product. The general selection of about 90% of the larger total surface reduction rate (see area reduction rate) and the smaller pass surface reduction rate (about 23%), to ensure the endurance of the product. On the high strength spring steel wire, pulling should be controlled each time the temperature of the steel wire outlet is lower than 150℃, to prevent the steel wire due to strain aging and change the crack, which is the main drawback of steel wire waste.

Because of the beauty, art, or in specific severe corrosion environment, galvanized layer can be applied to the above paint duplex system, as long as the paint system selection is correct, easy construction, its anticorrosion effect is 1.5~2.5 times better than the single paint and hot dip zinc life combined. With zinc layer to protect iron and steel, in addition to hot dip galvanizing method, there are several other methods, generally widely used, corrosion prevention effect is good and good economic benefits, hot dip galvanizing method.

Now most people buy barbed rope choose blade barbed rope, why is this? From the material blade barbed wire technology blade gill net is made of hot-dip galvanized steel plate or stainless steel sheet stamped out sharp knife sheet, high tension galvanized steel wire or blade barbed wire stainless steel wire as core wire combination of the resistance device. Because the gill net shape is not easy to contact, so it can achieve excellent protective barrier effect. The primary raw materials of products are galvanized sheet and stainless steel plate.

Therefore, the rust of galvanized black iron wire has a great relationship with storage. At the same time, after rust, it should also be reasonable for post-treatment to avoid affecting its use effect. Of course, when the black iron wire is galvanized, the thickness of the galvanized layer should be ensured, so that the possibility of rust can be reduced. Speaking of galvanized iron wire, perhaps many people think it is relatively rare, in fact, it is not.

Galvanized wire is processed from low carbon steel wire rod, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes. Galvanized wire is widely used. Electroplating temperature should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.

In order to pack and bundle galvanized wire on the surface of the deposit layer to remove the surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is caused by soaps and saponable fatty surfactants being brought into the tank. Moderate foam formation rates may be harmless. Small homogeneous particles of large denier present in the tank can stabilize the foam layer. To remove surface active substances by matting with activated carbon. Or filtration to make the foam less stable, which are effective measures; Other measures should also be taken to reduce the intake of surfactant. The electroplating speed can be significantly reduced by the introduction of organic matter. Although the chemical formula is conducive to a high deposition rate, the coating thickness cannot meet the requirements after the organic matter is loaded, so activated carbon can be used to treat the tank.