galvanized wire supplier

Galvanized wire is divided into hot dip galvanized iron wire and galvanized iron wire according to the production process. It has the characteristics of high tensile strength, good softness, zinc layer uniformity, corrosion resistance, beautiful color, good smoothness, strong adhesion and corrosion resistance. Hot dip galvanizing has better protective properties than electric galvanizing, so it is an important protective coating for steel parts used in harsh working conditions.

First, cold galvanized wire production process before treatment. Before galvanizing, a series of pre-treatment work on the steel wire is required, mainly including pickling, dissolution and brine or alkali washing.

Hot-dip galvanized wire is widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, electric power transmission, shipbuilding and other industries. It has been widely used in recent years in agricultural fields such as agricultural medicine sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and so on.

The material of small hexagonal mesh is the same as that of other hexagonal mesh, which is generally made of low carbon steel wire, stainless steel wire and galvanized steel wire as raw materials by the hexagonal mesh machine.

Different from the general zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach the former 6-8 times, so in the service life also has a great advantage, ordinary products three or five years began to corrosion and the latter will take longer to change. Stainless steel barbed rope is in the material aspect of protection, so the durability is also better, these two products are long in the service life, but in the price is high.

Hexagonal twist flower network is divided into heavy hexagonal network and small hexagonal network two categories. Both are made of steel wire braided with various materials, the difference is that the former uses thicker steel wire, and the latter uses finer steel wire braided.

Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device. In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc.

Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.

Now large roll galvanized wire in our life the use of more and more, to galvanized wire products bring a great market, galvanized wire products are more and more types. The surface coating of good quality galvanized wire is continuous and smooth. When the plating parts are installed and combined, there can be no flow hanging, slag or drop remaining, and no surface defects such as iron exposure. Good quality galvanized wire, coating must be uniform, roughly uniform in copper sulfate solution soaking five times without exposing iron. And with hammering test does not bulge, do not fall off. This is a good galvanized wire should have characteristics.