Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

That said, it can always deform by pulling hard without changing its integrity, so cold drawing has usually reached a limit, which is not a problem, because without this property it increases hardness, which is the desired effect. Cold wire drawing encountered more rain, when the climate is wet, easy oxidation and rust. Therefore, in the storage process should pay attention to avoid rust.