16 gauge iron wire

Hot dip galvanized wire is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, and the matrix metal forms the infiltration layer, the corrosion resistance is good, the outdoor environment of hot dip galvanized wire can be maintained for decades.

The hot plating wire is made of low carbon steel wire rod, which is processed by drawing forming, pickling and rust removal, high temperature annealing, hot dip galvanizing and cooling. Galvanized iron wire has resistance and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Widely used in construction, handicrafts, wire mesh, highway guardrail, commodity packaging and ordinary civilian and other fields.

Application: Mainly used in communication devices, medical equipment and braided mesh, brush, steel cable, filter screen, high pressure pipe, construction, technical products and other professional electric galvanized wire: is a low carbon steel as core wire, metal composite materials processed by wire drawing, electric galvanized technology.

Each coil of steel wire shall consist of one wire. The surface of the rod shall not have cracks, folds, scars, ears, layers or inclusions. However, indentation, pits, bumps, scratches and pockmarks are allowed, and the depth or height shall not be 0.2mm. There should be no corrosion and oxidation skin on the surface of the steel wire, and oxidation color is allowed by heat treatment. The surface of the wire is allowed to have scratches not exceeding half of the allowable deviation range of the diameter, and local defects not exceeding the allowable deviation of the appropriate diameter.

The tensile strength of cold drawn spring steel wire is slightly higher than that of oil tempered steel wire. The large specification of cold drawn steel wire elastic force is too large, winding the spring is very difficult, so the cold drawn spring steel wire application specification is generally less than 8.0mm, oil quenching tempered steel wire application specification is generally less than 13.0mm. In fact, the diameter of 13.0mm spring is used to light tension spring steel wire, cold drawing wound made into shape and then quenched and tempered. Steel wire with diameter above 15.0mm is mostly made by heating winding process.