  • 6, passivation to remove hydrogen parts should be passivation after the removal of hydrogen, passivation before the application of 1%H2SO4 or 1% hydrochloric acid activation 5~15s. Passivation shall be treated with colored chromate unless otherwise specified in the design drawings.

  • hot

  • In addition to these reasons, we should pay attention to the tooling and process must be stable, and regular testing should be done to ensure the uniformity of galvanized layer.

  • Zinc-coated wire is dipped in molten zinc with high production speed and thick but uneven coating. The thickness allowed by the market is 45 microns, the color is dark, the consumption of zinc metal, and the base metal to form infiltration layer, good corrosion resistance, hot dip galvanizing can be maintained for decades in the outdoor environment.