Third, 201 is high manganese content, the surface is very bright with dark bright, high manganese content is easy to rust. 304 contains more chromium, the surface is matte, no rust. Put the two together and you have a comparison. The most important thing is that the corrosion resistance is different. The corrosion resistance of 201 is very poor, so the price will be much cheaper. Because of the low nickel content of 201, the price is lower than 304, so the corrosion resistance is not as good as 304.

Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.