decorative stamped sheet metal panels

Every galvanized wire production into the peak season of the industry, the road to the factory will from time to time see transportation wire and container container vehicles, as well as galvanized bright silk short-distance transportation trucks, led to the utilization of labor in the surrounding countryside, solved the employment problem of most people. Galvanized wire is divided into hot plating wire and cold plating wire.

There is in place to use, the blade thorn rope is commonly border, installation and use of the fence, and prisons, and galvanized barbed wire is in the orchard, fence livestock and so on the installation of large area, although the use of relatively large, but not as good as the use of blade thorn rope and high grade, so this is also the main reason for the price is quite high. Finally, the general installation site of the blade barbed rope for the protection level requirements are relatively high, so the quality requirements for the product is also relatively high, but the ordinary galvanized barbed rope because of the requirements in the installation site is more casual, which is also for the processing process for the quality requirements are relatively low.

Large roll galvanized wire phosphating film is dark gray to black gray, the thickness is generally 5-20μm, has better corrosion resistance in the atmosphere. Membrane is a microporous structure, strong adsorption ability to paint, such as used as paint bottom, corrosion resistance can be further advanced. Metal oxidation treatment: Add steel products to NaOH and NaNO2 mixed solution, heating treatment, the surface can form a layer of thickness of about 0.5-1.5μm blue oxide film, in order to reach the purpose of steel corrosion prevention, this process is called blue treatment, referred to as blue.

Hot dip galvanizing is also called hot dip zinc and hot dip galvanizing: is an effective way of metal corrosion, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel parts is attached with zinc layer, so as to play the purpose of anticorrosion. Hot dip galvanizing process: finished product pickling – washing – adding bath aid – drying – hanging plating – cooling – drug – cleaning – grinding – hot dip galvanizing completion. Hot dip galvanizing is developed from the older method of hot dip galvanizing. It has a history of 140 years since it was applied to industry in France in 1836. However, the hot dip galvanizing industry has been developed on a large scale in the past 30 years with the rapid development of hot dip galvanizing wire.

Hot dip galvanized coating is also relatively thick, but there is an uneven situation, for example, the thickness of the thin is only 45 microns, thick can reach 300 microns or even thicker, the color of this product is relatively dark. There is also a lot of zinc consumed in the production process. Zinc will form an infiltration layer with the metal. Its advantage is that it has good corrosion resistance. Electrogalvanizing, it is through the plating tank in the zinc one-way plating on the outside of the metal products, this way of making products is relatively slow, but its thickness is more uniform.

Blade thorn rope because the volume is relatively large, so the thorn rope factory is used to packaging treatment.