In order to remove defects such as surface film layer and surface inclusion of large roll galvanized wire, it can be treated by conventional technology. The presence of small homogeneous particles of large denier in the tank can stabilize the foam layer, but the accumulation of too many solid particles can cause explosion. Activated carbon mat to remove surface active substances, or through filtration to make the foam less stable, these are effective measures; Other measures should also be taken to minimize the intake of surface active substances. The electroplating speed can be significantly reduced by the introduction of organic matter.

The principle of hot dip galvanizing is simply that clean iron parts are immersed in a zinc bath through Flux wetting, so that the steel reacts with molten zinc to produce an alloyed skin film.

The diameter of the wire is generally 0.3mm – 3mm, after the wire is not very strong, need to annealing, annealing this step is very important, can ensure the production of galvanized welding net, with good elasticity and toughness. After welding, the welding mesh becomes black wire welding mesh and can not be put on the market, because its corrosion resistance is poor and the service life is short, so it needs to be galvanized or dipped plastic treatment.

The most obvious gap in a short period of time is the cross section of this piece, hot dip galvanized wire because it is surface anti-corrosion treatment, so in the cross section of this piece will appear rust, and stainless steel wire because the internal raw materials and surface raw materials are consistent, so there is no such situation.

M