Different from common zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach 6-8 times of the former, so there is a great advantage in the service life, ordinary products begin to corrosion three to five years while the latter will take longer to change. Stainless steel barbed rope is in material protection so durability is also better, these two products are long service life, but in terms of high price.

The composition of hot dip galvanizing layer is composed of hot dip galvanizing layer, which is composed of iron zinc alloy between iron matrix and surface pure zinc layer. The shape of the workpiece is formed by the iron zinc alloy layer in hot dip, so that the iron and pure zinc layer touch outstanding. When the iron workpiece is immersed in a molten zinc solution, the initial zinc and iron (body) are formed at the interface. This is a crystal made up of zinc atoms in the solid metal iron. When two metal atoms are fused together, the gravitational force between the atoms is very small.

In moist air, a dense basic zinc carbonate film forms on the surface of zinc. Zinc coating belongs to the anodic coating, it is mainly used to prevent the corrosion of steel, its protective performance and the thickness of the coating is very important. The protective and decorative properties of zinc coating can be improved significantly after passivation treatment, dyeing or coating with light protection agent.

In addition, hot-dip galvanized wire also needs to pay attention to maintenance and maintenance during use. Although it has good corrosion resistance, the zinc-iron alloy protective layer of hot-dip galvanized wire will gradually wear out after a long time of use. Therefore, regular inspection and maintenance of the surface of hot-dip galvanized wire, such as recoating or anti-corrosion treatment, helps to extend its service life.