ornamental perforated sheet metal

First of all, the protective layer of zinc-iron alloy can prevent the steel wire from being corroded by oxidation. The zinc metal reacts with water and oxygen to form a dense zinc oxide layer, which forms a physical barrier to prevent oxygen and water from entering the inside of the steel wire, reducing the chance of corrosion. Compared with ordinary steel wire, hot-dip galvanized wire is more resistant to corrosion in humid, high humidity or corrosive environments such as acid and alkali, so it is more durable.

Since galvanized iron wire will rust, we need to pay attention in the process of storage and use, try to store in a dry and ventilated environment, in the process of use to avoid damaging the surface of galvanized iron wire, we can slow down the time of galvanized iron wire rust.

There are too many fake things on the market now, so shoppers should learn how to distinguish the quality of galvanized wire, the right to protect their consumers’ rights and interests. Galvanizing process of galvanized wire products is a very effective metal anticorrosion method, and it is also widely used in other industrial fields. After galvanizing, iron wire is commonly used in metal structure equipment of various industries.

The application of electric welding net is more widely, at present it has replaced the use of other parts of the wire mesh, the cost of electric welding net is lower, the production speed is very fast, so it is very popular. Welding net galvanized before the need for processing is recrystallization annealing, because the welding net must maintain a no oxide and no other impurities of pure iron active surface, if you can not keep its surface clean will lead to a bad galvanizing effect, galvanized layer and iron material is not closely combined, so this step is necessary.

Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, The softness is also very uniform, the color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry, etc.

If the coating roughness is not caused by the above reasons, it may be caused by impurities in the plating solution. Can take a small amount of electroplating solution, filtration test, and then take a small amount of electroplating solution, with zinc powder treatment after the test, check the problem is solid particles or copper, lead and other foreign metal impurities caused by. One by one, it’s not hard to find the cause of the problem. Galvanized iron wire coating blister, poor adhesion.

Wire factory reminds you in the purchase of galvanized wire, should be stored in dry, ventilated conditions, do not contain corrosive gases, do not mix with organic volatile gas produced paint, plastic and other substances in a good environment. If possible, we can add reliable inner packaging for galvanized parts, and put desiccant. If the zinc layer of white spots and long hair, can only be removed by mechanical methods, and then normal passivation, or completely washed off the zinc layer after re-plating.

Defects such as surface film and surface inclusions can be found and treated by conventional techniques in order to remove them locally from the surface of the deposition layer. Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank.

3, hexagonal network customized weight, the greater the weight, the more sufficient the material.

Galvanized wire is processed from low carbon steel wire rod, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes. Galvanized wire is widely used. Electroplating temperature should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.