v wire screen

The hot plating wire is made of low carbon steel wire rod, which is processed by drawing forming, pickling and rust removal, high temperature annealing, hot dip galvanizing and cooling. Galvanized iron wire has resistance and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Widely used in construction, handicrafts, wire mesh, highway guardrail, commodity packaging and ordinary civilian and other fields.

On the contrary, the denser the ion deposition, the better the quality of zinc layer. Under the condition that the surface zinc layer is dense and bright, the quality of zinc layer per unit area should reach 80g/m2, and the process parameters should be optimized as follows: current density is 16-20A /dm2, mass concentration of zinc sulfate solution is 500g/L, and pH value is 2.5-3.0.

Most people think that the fine wire of the front and back twist barbed wire is not as thick and durable as common sense, but the front and back twist barbed wire is made of hot-dip galvanized steel wire, which is more than three times greater than the tensile strength of iron wire, and the amount of zinc added is not less than hot-dip wire

Through drawing forming, pickling rust removal, high temperature annealing, hot dip galvanizing. Cooling process and other processing. Electric galvanized iron wire selection of high quality low carbon steel as raw material, after drawing, galvanizing and other processes completed. It has the characteristics of galvanized layer, strong corrosion resistance and strong galvanized layer, etc. Electric galvanized iron wire is widely used in construction, highway wall, tie-flower, net weaving and other industries.