The use of spring in a specific environment, there will be some special requirements for steel wire, such as: the use of spring in corrosive media, must have good corrosion resistance function. Precision instruments used in the spring, should have long-term stability and sensitivity, temperature coefficient to be low, high quality elements, after effect to be small, elastic modulus to be stable.
The spring operating at high temperature requires that it can adhere to the elastic limit and good creep resistance at high temperature. In addition, the forming process and heat treatment process of spring steel wire should also be considered. Cold drawn spring steel wire and oil quenched tempered spring steel wire are directly around the supply of steel wire spring, spring forming after the elimination of stress directly used.
The tensile strength of cold drawn spring steel wire is slightly higher than that of oil tempered steel wire. The large specification of cold drawn steel wire elastic force is too large, winding the spring is very difficult, so the cold drawn spring steel wire application specification is generally less than 8.0mm, oil quenching tempered steel wire application specification is generally less than 13.0mm. In fact, the diameter of 13.0mm spring is used to light tension spring steel wire, cold drawing wound made into shape and then quenched and tempered. Steel wire with diameter above 15.0mm is mostly made by heating winding process.
Carbon spring steel wire current national and occupational recommendation specifications are divided into two types: one is cold deformation steel wire, also known as cold tension spring steel wire. Cold drawn carbon spring steel wire is first quenched by lead to obtain soxhlet arrangement, and then the surface phosphating, with a large surface reduction rate drawn to the finished scale, the steel wire arrangement is fibrous, has high tensile strength and elastic limit, good winding and change function.
Post time: 09-09-22